Mixing: Each set includes proper amount of component A and B. Entire quantity of component B is added to component A and mixed. Component B is a viscous liquid so it flows hardly in cool weather. The mixture is prepared by stirring for 3-5 min. and using a low speed electric stirrer (200-400 rpm). The stirrer is adducted to sides of the can to achieve a homogenous mixture. The stirrer must be at a sufficient depth in the packaging to prevent air admission. In case the stirrer is brought very closer to the surface, air bubbles may occur and waterproofing properties of Emülzer® HDM PU 2K may be reduced. The pot life is between 30-45 min. at 20°C temperature. However, it is recommended to work with applicable amount in 1/2 hour. The mixture must be used in 30 minutes, otherwise irreversible gelation will begin. Reduction of viscosity and elongation show the end of the pot life. The material that is in this situation should not be used.

Filling The Joints: The joint must be filled from the bottom to the top with a suitable tool, also the material should be completely in contact with side surfaces. The joints which are filled should be checked in 10-20 min. Excess of the material must be scraped with a spatula and the empty places must be filled immediately. If the slope of the joint is greater than 2%, the horizontal barrier bars should be placed at regular intervals. When the material that is applied between the bars is tolerably cure, the bars are taken off and the resulting gaps are filled. Emülzer® HDM PU 2K has resistance to traffic after it has been cured (approximately 48 hours later), also it has resistance to chemicals 7 days later (at 20°C). The area which is applied with Emülzer® HDM PU 2K must be prevented from water for 6-8 hours.